Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultramid® B3ZG6 - PA6-I-GF30 - BASF

Check here, which other Ultramid B datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - 材料特有の特性 - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

An impact-modified, glass fibre reinforced injection molding grade for industrial items requiring very high impact stregth and rigidity, used e.g. for automobile airbag housings and half-shells for suitcases.
The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change.

Processing/Physical Characteristics	乾燥/調湿	単位	テスト基準
ISO データ
メルトボリュームレイト, MVR	20 / *	cm³/10min	ISO 1133
温度	275 / *	°C	-
荷重	5 / *	kg	-
成形収縮率, 平行	0.3 / *	%	ISO 294-4, 2577
成形収縮率, 直角	0.7 / *	%	ISO 294-4, 2577

機械的特性	乾燥/調湿	単位	テスト基準
ISO データ
引張弾性率	8950 / 5180	MPa	ISO 527
破壊応力	170 / 96	MPa	ISO 527
破壊ひずみ	4.4 / 10.8	%	ISO 527
引張クリープ弾性率, 1h	* / 3800	MPa	ISO 899-1
引張クリープ弾性率, 1000h	* / 3000	MPa	ISO 899-1
シャルピー衝撃強さ, +23°C	100 / 119	kJ/m²	ISO 179/1eU
シャルピー衝撃強さ, -30°C	102 / 107	kJ/m²	ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C	20.2 / 33.8	kJ/m²	ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C	11.3 / 11.1	kJ/m²	ISO 179/1eA

熱的特性	乾燥/調湿	単位	テスト基準
ISO データ
溶融温度, 10°C/min	220 / *	°C	ISO 11357-1/-3
荷重たわみ温度, 1.80 MPa	200 / *	°C	ISO 75-1/-2
荷重たわみ温度, 0.45 MPa	220 / *	°C	ISO 75-1/-2
ビカット軟化温度, B	220 / *	°C	ISO 306
線膨張係数, 平行	21 / *	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	116 / *	E-6/K	ISO 11359-1/-2
1.5mm厚さでの燃焼性	HB / *	class	IEC 60695-11-10
試験片の厚さ	1.6 / *	mm	-
Yellow Card 可用	はい / *	-	-
厚さhでの燃焼性	HB / *	class	IEC 60695-11-10
試験片の厚さ	0.7 / *	mm	-
Yellow Card 可用	はい / *	-	-
酸素指数	23 / *	%	ISO 4589-1/-2

電気的特性.	乾燥/調湿	単位	テスト基準
ISO データ
比誘電率, 1MHz	3.8 / 6.8	-	IEC 62631-2-1
誘電正接, 100Hz	200 / 2200	E-4	IEC 62631-2-1
誘電正接, 1MHz	200 / 2000	E-4	IEC 62631-2-1
体積抵抗率	1E13 / 1E10	Ohm*m	IEC 62631-3-1
表面抵抗率	* / 1E10	Ohm	IEC 62631-3-2
耐電圧	46 / 38	kV/mm	IEC 60243-1
耐トラッキング性	- / 600	-	IEC 60112

その他の特性.	乾燥/調湿	単位	テスト基準
吸水率	6.2 / *	%	Sim. to ISO 62
吸湿率	2 / *	%	Sim. to ISO 62
密度	1330 / -	kg/m³	ISO 1183

材料特有の特性	乾燥/調湿	単位	テスト基準
ISO データ
粘度数	160 / *	cm³/g	ISO 307, 1157, 1628

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	80	°C	-
Pre-drying - Time	4	h	-
Processing humidity	≤0.15	%	-
樹脂温度	270 - 290	°C	-
金型温度	80 - 90	°C	-

機能

特殊な特性

成形加工法.

射出成形.

納入形状.

ペレット.

添加剤.

滑剤., 離型剤.

特殊な特性.

高耐衝撃及び耐衝撃改良., 熱安定化.

領域別の利用可能性

北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ

その他の情報

村遜速揃

PREPROCESSING
Pre/Post-processing, max. allowed water content: .15 %
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 4 h

PROCESSING
injection molding, Melt temperature, range: 270 - 290 °C
injection molding, Melt temperature, recommended: 280 °C
injection molding, Mold temperature, range: 80 - 90 °C
injection molding, Mold temperature, recommended: 80 °C
injection molding, Dwell time, thermoplastics: 10 min

耐薬品性

酸
	5wt％酢酸 (23ﾟC)
	10wt％クエン酸 (23ﾟC)
	10wt％乳酸 (23ﾟC)
	36wt％塩酸 (23ﾟC)
	40wt％硝酸 (23ﾟC)
	38wt％硫酸 (23ﾟC)
	5wt％硫酸 (23ﾟC)
	40wt％硝酸 (23ﾟC)
塩基
	35wt％水酸化ナトリウム (23ﾟC)
	1wt％水酸化ナトリウム (23ﾟC)
アルコール
	イソプロピルアルコール23℃ (23ﾟC)
	メタノール　23℃ (23ﾟC)
	エタノール　23℃ (23ﾟC)
炭化水素
	ヘキサン (23ﾟC)
	トルエン (23ﾟC)
	イソオクタン (23ﾟC)
ケトン系溶剤
	アセトン (23ﾟC)
エーテル溶剤
	ジエチルエーテル (23ﾟC)
鉱油
	SAE 10W40 マルチグレードモーターオイル (23ﾟC)
	SAE 10W40 マルチグレードモーターオイル (130ﾟC)
標準燃料
	ディーゼル燃料（ISO 1817液F) (23ﾟC)
	ディーゼル燃料（ISO 1817液F) (>90ﾟC)
食塩水
	10wt％塩化ナトリウム (23ﾟC)
	10wt％次亜塩素酸ナトリウム (23ﾟC)
	50wt％ジンクロメート (23ﾟC)
その他
	エチルアセテート (23ﾟC)
	過酸化水素 (23ﾟC)
	DOT No.4ブレーキ液 (130ﾟC)
	50wt%エチレングリコール水溶液 (108ﾟC)
	水 (23ﾟC)

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.